Axson F38 offers excellent impact resistance, is very low viscosity with a thermoplastic aspect. With a low shrinkage ratio, short demould time and good ability for painting, this resin is widely used within the small prototype and scale model industry. The F38 has a pot life of 2 minutes and a demould time of 20 - 25 minutes with a full cure of around 72 hours.
- Fast Demoulding Time
- Low Chemical Attack Towards Silicone Moulds
- Good Ability For Being Painted
|Axson F38 ||Unit |
|Mix Ratio By Weight ||100A : 100B |
|Pot Life @ 25°C ||2 mins |
|Demould Time ||20 mins |
|Shore D Hardness ||D72 |
|Mixed Viscosity mPas ||35 |
|Flexural Strength Mpa ||48 |
|Flexural Modulus Elasticity ||750 mpa |
|Maximum Casting Thickness ||5mm - 10mm |
|Glass Transition Temp ||55°C |
|Cure Colour ||Off White / Cream |
For best results ensure resins and moulds are at temperature above 18°C before using, using at colder temperatures will effect cured characteristics and may inhibit cure. Ensure moulds are free from dust and other contaminants. Always perform small test before pouring large amounts to ensure suitability. F38 is extremely moisture sensitive, keep containers closed when not in use. When stored correctly unopened product has a shelf life of 3 months from purchase. Please refer to technical data sheets for further information regarding usage.