AROPOL M 105 TAXR is a thixotropic, pre-accelerated, ortophthalic acid based polyester resin with short gel time and low peak exotherm.
When applying AROPOL M 105 TAXR resin, emission is reduced by up to 50% compared to standard resin. Emission is only 2-5% of polyester resin used compared to 5-10% of standard polyester resins. Excellent glass fibre wet out properties and easiness of application is characteristic for AROPOL M 105 TAXR.
Application and Use
AROPOL M 105 TAXR resin is suitable for spray-up, hand lay-up and filament winding methods for manufacturing numerous FRP products for the marine, building and construction and transportation markets. Curing characteristics of AROPOL M 105 TAXR allow building laminates of thickness 3-12 mm wet on wet.
Property at 23 C | Typical value |
Viscosity, Brookfield RV2, 10 rpm | 1400 mPas |
Viscosity, Cone & Plate | 180 mPas |
Density | 1,1 kg/dm3 |
Geltime, 1% M50 | 25 min |
Peak Exotherm | 80 °C |
Certificates and Approvals
AROPOL M 105 TAXR resin is approved by Lloyd's Register and complies with the requirements of ISO 12215-1 standard for construction of small crafts.
The manufacturing, quality control and distribution of products are complying with one or more of the following programs or standards: ISO 9001, ISO 14001 and OHSAS 18001.
Please note - Polyester resins are best used within six months from date of purchase.
*Although this product is described as Clear, it is in-fact translucent blue in colour, The term 'Clear' is a grp industry standard as it is an non pigmented material, This does not create a completely translucent or water clear effect.*