High strength silicone mold making rubbers with improved mold life for polyester resins. Our silicone has been formulated for easy mixing by hand, with colour coded component giving a visual aid to ensure mixing is adequate. The two components mix easily and because of the low viscosity most grades can be used without processing in a vacuum chamber. This silicone is suited for the detailed reproduction of figures, art objects and similar items.
Improved mould life for polyester resins
Outstanding release properties
High Flowabilty and long woring time
High tear resistance
High elasticity for easy removal of complex replica parts
Can be made thixotropic (non flowable) for vertical surface replication
|Mix Ratio by Weight ||10 : 1 |
|Working Time ||40 - 60 Minutes |
|Curing Times ||6 - 8 Hours @ 25°C |
|Cured Colour ||Light Pink |
|De-Mould Time ||12 - 24 Hours |
|Mixed Viscosity mPas ||13000 |
|Hardness Shore A ||13 |
|Tensile Strength Mpa ||3.7 |
|Elongation @ Break % ||585 |
| Tear Strength kN/m ||28 |
|Linear Shrinkage ||0.2-0.4 |
|Base Colour ||Off - White |
275g kit = 250g Silicone - 25g Catalyst
550g kit = 500g Silicone - 50g Catalyst
1.1kg kit = 1kg Silicone - 100g Catalyst
2.2kg kit = 2 x 1kg Silicone - 2x 100g Catalyst
5.5kg kit = 5kg Silicone - 500g Catalyst
11kg kit = 2 x 5kg Silicone - 2 x 500g Catalyst
22kg kit = 20kg Silicone - 2kg Catalyst
250g of Silicone will fill approximately 200ml by volume
Instructions & datasheet downloads available under Technical & Safety Sheets on the tab above.
Please note this silicone is not suitable for food use. It is also not suitable for direct use on skin.
Base and catalyst use universal containers for various kit sizes and are supplied by weight, while the supplied containers may not be full, they will contain the correct amount of both base and hardener according to the listing. At point of packaging and dispatch lids may be taped to prevent damage or spillage during transportation.