Polycraft EP01 Epoxy Modeling Paste

Polycraft EP01 Epoxy Modeling Paste
Zoom  Zoom
Our Price:  £20.00(Inc. 20% VAT)(£16.67 Exc. VAT)Earn 20 Loyalty Points

Quick Link Code:  5911
Brand:  Polycraft

Filler Mixing Board - Plain WhiteFiller Mixing Board - Plain White
Plastic SpreadersPlastic Spreaders

*Image(s) For Illustration Purpose Only


Epoxy modeling paste can be used by hand in 10 to 40 mm coat on a rough form and used for style mock-ups, high dimension models, slight checking fixtures.

Just mix both parts by squeezing together to give a smooth putty like material and mould accordingly.


  • Mixing ratio by weight : 1/1 Mixing by hand or mechanical
  • Mixing Can be applied until 40 mm per coat
  • Quick hardening in thin coat
  • Adhesion on different supports such as wood, foam, machinable slabs, polystyrene, etc.
  • Modifications and re-filling possible with EP01 (support has to be sand first)
  Resin Hardener Mixed
Mixed Ratio By Weight 100 100  
Aspect Paste Paste Paste
Colour White Light Red Light Red
Specific gravity at 25°C 0.51 0.54 0.53
Pot life at 25°C on 250 g     55 Min


Mix the two components by hand or with a planetary mixer according to the indicated ratio. When homogenising apply the paste by pressing on the rough form. Let cure 12 hours to 16 hours at room temperature before machining. To improve the finishing, it is possible to smooth the surface with water or alcohol.


Normal health and safety precautions should be observed when handling these products:
: ensure good ventilation
: wear gloves and safety glasses
For further information, please consult the product safety data sheet.


Shelf life of both parts is 12 months in a dry place and in their original unopened containers at a temperature between 15 to 25°C. Any open can must be tightly closed under dry inert gas (dry air, nitrogen, etc.).